Stainless steel belts | Colzani TRANSBANDA 18500 |
CHARACTERISTICS
AND DIMENSIONS
Physical and mechanical properties (Typical values)
|
|
TRANSBANDA
18500
|
|
Type
|
|
Cr Ni
17 7
|
|
Similar
Material
|
|
DIN
1.4310 / AISI 301
|
|
Yield strength
.2 at 20ºC
|
Kg./mm2
|
110-120
|
|
Tensile
strength 20ºC
|
Kg./mm2
|
125
|
|
Hardness
|
Rockwell
C
|
34-37
|
|
Modulus of
elasticity
|
Kg./mm2
|
18.500
|
|
Thermal
contuctivity
|
Kcal./m.h.ºC
|
13
|
|
Specific heat
|
Cal/ºC
|
0.12
|
Transbanda
18500 is similar to: Sandvik 1200
SA / Berndorf Band Nicro 12.1
Weights per meter and dimension
|
TRANSBANDA
18500
Stainless steel belts
|
|
(MM.)
|
0.6
|
0.8
|
1.0
|
1.2
|
1.6
|
|
100
|
0.48
|
0.63
|
0.79
|
|
|
|
200
|
0.96
|
1.27
|
1.58
|
|
|
|
300
|
1.45
|
1.90
|
2.37
|
|
|
|
400
|
1.92
|
2.53
|
3.16
|
|
|
|
500
|
2.40
|
3.17
|
3.95
|
|
|
|
600
|
2.90
|
3.80
|
4.75
|
5.80
|
|
|
700
|
3.78
|
4.43
|
5.54
|
6.77
|
|
|
800
|
3.85
|
5.06
|
6.32
|
7.70
|
|
|
900
|
|
5.70
|
7.12
|
8.70
|
|
|
1000
|
|
6.32
|
7.90
|
9.60
|
12.64
|
|
1100
|
|
6.97
|
8.71
|
10.63
|
13.93
|
|
1200
|
|
7.60
|
9.50
|
11.60
|
15.12
|
|
1300
|
|
|
10.29
|
12.57
|
16.47
|
|
1400
|
|
|
11.08
|
13.53
|
17.73
|
|
1500
|
|
|
11.90
|
14.40
|
19.00
|
|
1550
|
|
|
12.30
|
14.90
|
19.60
|
Belts can be welded at our works before dispatch or in site when the
belt is installed. Transverse welded seams can be performed at right
angles or at sloping angle to the edge of the belt.
Steel belts can be joined by means of rivets. For belt thickness 0,6 mm
rivet diameter is 2,7 mm or 4,8 mm on request. For belt thickness over
0,6 mm, the rivet diameter is 4,8 mm. Both carbon and stainless steel
belts can be supplied with perforations. For continuous drying,
cooling, cooking and dehydration, perforated belts are available with
open areas up to 40% of the total surface.
|